Abstract: The main aim of presented work was the commencing the tests and analysis of the DLC type a:C:H coatings obtained with PACVD technique on the elements from Co-Cr-Mo alloys., among others: monitoring of structure changes, hardness measurement, estimation of the surface geometrical structure and tribologic tests. The analysis of surface structure and its elementary composition were estimated with the application of scanning SEM microscope, as well as TEM transmission microscope. The hardness of the elements with and without the coating was measured with the Matsuzawa micro hardness testing tester. Tribologic test of materials wear resistance was done with using T-01M apparatus ball-on-disc type, within a set of Al2O3 ball - disk from Co-Cr-Mo alloys with DLC coating, in technologically dry friction condition as well as with Ringer solution lubrication. Friction tests were conducted with using tester T-17, working in association: polymer pin made of high-molecular polyethylene PE - UHMW - plate from Co-Cr-Mo alloys with DLC coating with Ringer solution lubrication. The results obtained during mentioned above tests showed that the application of DLC coatings greatly enhances the operating features of the coated surfaces.
B I B L I O G R A F I A[1] FORSICH C., HEIM D., MUELLER T., 2008, Influence of the deposition temperature on mechanical and tribological properties of a-C:H:Si coatings on nitrided and postoxidized steel deposited by DC-PACVD. Surface & Coatings Technology, 203, 521-525.
[2] POPOV C., KULISCH W., BLIZNAKOV S., MEDNIKAROV B., SPASOV G., PIROV J., JELINEK M., KOCOUREK T., ZEMEK J., 2007, Characterization of the bonding structure of nanocrystalline diamond and amorphous carbon films prepared by plasma assisted techniques. Applied Physics A 89, 209-212.
[3] BOSMAN, M., KEAST Y., WATANABE M., McCULLOCH D., SHAKERZADEH M. TEO E., TAY B., 2009, Quantitative, nanoscale mapping of sp2 percentage and crystal orientation in carbon multilayers. Carbon, 47, 94-101.
[4] PAUL R, DALUI S., DAS S.N., BHAR R., PAL A.K., 2008, Hydrophobicity in DLC films prepared by electrodeposition technique. Applied Surface Science, 255, 1705-1711.
[5] OZIMINA D., MADEJ M., 2010, Assessment of properties of one- and multilayers coats DLC,. Tribologia, 2, 119-135, (in Polish).
[6] FERRARI, A. AND ROBERTSON J., 2000, Interpretation of Raman spectra of disordered and amorphous carbon. Phys. Rev. B 61, 14095-14107. 
Pełny tekst 
YADDA/CEON