Impact of operating conditions on the strength and frequency of destruction of fibre-cement composites

Czasopismo: ARCHIVES OF CIVIL ENGINEERING   Tom: LXVII, Zeszyt: 2, Strony: 67-83
ISSN:  1230-2945
Opublikowano: Czerwiec 2021
 
  Autorzy / Redaktorzy / Twórcy
Imię i nazwisko Wydział Katedra Do oświadczenia
nr 3		 Grupa
przynależności		 Dyscyplina
naukowa		 Procent
udziału		 Liczba
punktów
do oceny pracownika		 Liczba
punktów wg
kryteriów ewaluacji
Anna Adamczak-Bugno orcid logo WBiAKatedra Wytrzymałości Materiałów i Analiz Konstrukcji Budowlanych *Takzaliczony do "N"Inżynieria lądowa, geodezja i transport5050.0050.00  
Aleksandra Krampikowska orcid logo WBiAKatedra Wytrzymałości Materiałów i Analiz Konstrukcji Budowlanych *Takzaliczony do "N"Inżynieria lądowa, geodezja i transport5050.0050.00  

Grupa MNiSW:  Publikacja w czasopismach wymienionych w wykazie ministra MNiSzW (część A)
Punkty MNiSW: 100

Pełny tekstPełny tekst     DOI LogoDOI    
Keywords:

fibre-cement composites  ventilated faades  acoustic emission method  bending strength 


Abstract:

The paper examines the impact of possible operational factors on strength and frequency parameters generated by bending of fibre-cement panels. The tests were performed on elements cut out of a standard
commercially available panel. The samples were exposed to factors described as environmental (soaking in water, bath-drying cycles, freeze-thawing cycles) and unique (flame ignition and high temperature exposure) and then
subjected to three-point bending tests. Acoustic emission (AE) signals were acquired during the external load application. After the measurements were completed, the strength of individual elements was determined and the frequencies generated during bending were calculated. The obtained results were analysed statistically. Comparing the results obtained for a group of samples subjected to environmental and unique factors, significant differences between them were noted. It was noted that the decrease in the strength of the samples is related to the emission of lower frequency sounds. It was found that the application of the presented methodology allows to determine the condition of the fibre-cement boards in use.